MICROLON 8114
CORROSION RESISTANCEThe data presented below is intended to be used only as a guide. To represent what
testing has been performed and documented. All tests were conducted at room temperature
except as noted. It is advisable to subject the coating to your test procedures prior to
its use in any chemical environment.
| CHEMICAL |
CONCENTRATION % |
HOURS |
WATER
Deionized - Boiling
Salt (immersed)
Salt (spray)
Tap |
100
30
5
250F/120C @ 10,000 psi 100 |
1000
4000
1000
24 |
ACIDS
Hydrochloric
Hydrochloric
Hydrochloric
Hydrochloric(125F/50C)
Sulfuric
Nitric
Picric |
36
15
2ph
2ph
25
35
saturated solution |
24
150
300
300
1500
24
120 |
BASE
Caustic
Caustic
Caustic
Caustic(125F/50C) |
2
100
12.5 pH
9.5 pH |
24
336
150
300 |
PHYSICAL PROPERTIES
| |
UNITS |
VALUES |
| Tensile Strength |
psi |
2,000 - 4,000 |
| Elongation |
% |
35 - 50 |
| Water Absorption |
% |
0.03 |
| Service Temperature Continuous |
oF/oC |
500\260 |
| Service Temperature Intermittent |
oF/oC |
550\285 |
| Pencil Hardness |
H |
6H |
| Dielectric Strength |
V/MIL |
1,200 - 2,000 |
| Wear Resistance (K-factor) |
cu.in. - min. X 10(-10)
1 lb.-ft.-hr. |
6-8 |
|
|
|